Monel 400 Uns N04400 W.Nr. 2.4360 U 2.4361
Kompożizzjoni Kimika
| Liga | element | C | Si | Mn | S | Ni | Fe | Cu |
| Monel 400 | Min | 63.0 | 28.0 | |||||
| Max | 0.3 | 0.5 | 2.0 | 0.024 | 2.5 | 34.0 |
Proprjetajiet Mekkaniċi
| Status Aolly | Saħħa tat-tensjoni Rm Mpa Min | Saħħa ta 'rendiment RP 0. 2 Mpa Min | Titwil A 5 % Min |
| Soluzzjoni | 745 | 325 | 40 |
Proprjetajiet Fiżiċi
| Status Aolly | Saħħa tat-tensjoni Rm Mpa Min. | Qawwa tar-rendiment RP 0. 2 Mpa Min. | Titwil A 5 % |
| ittemprat | 480 | 170 | 35 |
Standard
Vireg, Bar, Wajer u Forġa Stokk- ASTM B 164 (Virga, Bar, u Wajer), ASTM B 564 (Forġar)
Pjanċa, Folja u Strixxa-,ASTM B 127, ASME SB 127
Pajp u Tubu- ASTM B 165 (Pajp u Tubu mingħajr saldatura), ASTM B 725 (Pajp iwweldjat), ASTM B 730 (Tubu Iwweldjat), ASTM B 751 (Tubu Iwweldjat), ASTM B 775 (Pajp iwweldjat), ASTM B 829 (Pajp Iwweldjat u Tubu)
Prodotti tal-Iwweldjar- Filler Metal 60-AWS A5.14/ERNiCu-7; Elettrodu tal-Iwweldjar 190-AWS A5.11/ENiCu-7.
Karatteristiċi ta 'Monel 400
● Reżistenti għall-ilma baħar u l-fwar f'temperaturi għoljin
● Reżistenza eċċellenti għall-ilma salmastru li jiċċirkola malajr jew ilma baħar
● Reżistenza eċċellenti għall-qsim tal-korrużjoni tal-istress fil-biċċa l-kbira tal-ilma ħelu
● Partikolarment reżistenti għall-aċidi idrokloriku u idrofluworiku meta jkunu de-arjati
● Joffri xi reżistenza għall-aċidi idrokloriku u sulfuriku f'temperaturi u konċentrazzjonijiet modesti, iżda rari huwa l-materjal magħżul għal dawn l-aċidi
● Reżistenza eċċellenti għall-melħ newtrali u alkalin
● Reżistenza għall-iklorur indott stress korrużjoni cracking
● Proprjetajiet mekkaniċi tajbin minn temperaturi taħt iż-żero sa 1020 ° F
● Reżistenza għolja għall-alkali
● Preċedenti: Liga N-155
● Li jmiss: Monel k-500 UNS N05500/ W.Nr. 2.4375